In the recently published ‘Additive Manufacturing of Information Carriers Based on Shape Memory Polyester Urethane’ Dilip Chalissery, Thorsten Pretsch, Sarah Staub, and Heiko Andrä explored more in the 4D printing realm.
Shape memory polymers are becoming more and more useful today as they can respond to their environment, whether in terms of temperature or moisture and can be 3D printed in complex geometries. For this research, thermoresponsive polyurethane-based SMPs are printed using FDM (also called FFF) 3D printing, which has been relatively rare in research so far. The team created two sample designs for their study: one in the form of a QR code reading Fraunhofer IAP, and the other a cylindrical granulate grain.
An Ultimaker 3 was used for fabrication, with samples heated to 100 ◦C and then cooled to −100 ◦C, with the process repeated twice. The QR code was represented in three different types:
- Type 1 – The substrate was printed with non-dyed PEU using a 400 µm nozzle and a target layer thickness of 180 µm.
- Type 2 – the substrate was printed with non-dyed PEU using a 400 µm nozzle. Again, a target layer thickness of 180 µm was selected for the substrate, but the elevation was built with red PEU employing a 400 µm nozzle.
- Type 3 – the substrate was also printed with non-dyed PEU using a 400 µm nozzle, but this time a reduced target layer thickness of 15 µm was selected.
“For all experiments, heating and cooling rates of 3 ◦C·min−1 were selected and the holding time at the highest and lowest temperature was set to 10 min. The storage modulus (E´), loss factor (tan δ) and the glass transition temperature (Tg) were determined for the second heating. The phase transition behavior of the PEU was also studied by differential scanning calorimetry (DSC) using a Q100 DSC from TA Instruments (New Castle, DE, USA),” explained the authors.
The researchers offered a comprehensive study, examining the following:
- Thermal properties
- Print quality
- Programming and characterization of SMPs
While some inaccuracies were found in the 3D prints, the QR codes were functional and as they triggered the shape memory, it deformed correctly, along with providing machine readability as required. The authors stated that shape memory properties were so good, they went on to wonder if they could endure even stronger deformations—with the sample proving so in a stable manner.
The QR codes were significantly light in weight, and they found a good balance in build rate and print resolution with FFF 3D printing, thus making it a ‘promising technology’ for fabrication of SMPs in innovative new shapes.
“The main advantages of the new manufacturing process for QR code carriers are that polymer extrusion can be easily controlled, a significantly lower amount of base material is needed, facilitating the fabrication of very thin layers with a thickness below 10 µm, and the use of solvents can be avoided,” concluded the researchers.
“All these aspects emphasize that the novel production process for QR code carriers is not only attractive for research purposes, but also from an economic point of view, not least because the material could be qualified for processing with a commercially available 3D printer. Therefore, FFF could turn out as an enabling technology to realize applications for SMPs in fields like counterfeit-proof marking of goods at risk of plagiarism and supervision of cold chains.”
Shape memory polymers have been used today for making soft actuators, 4D structures from silicone materials, metamaterials, and more. What do you think of this news? Let us know your thoughts! Join the discussion of this and other 3D printing topics at 3DPrintBoard.com.
Subscribe to Our Email Newsletter
Stay up-to-date on all the latest news from the 3D printing industry and receive information and offers from third party vendors.
You May Also Like
Gorilla Sports GE’s First 3D Printed Titanium Cast
How do you help a gorilla with a broken arm? Sounds like the start of a bad joke a zookeeper might tell, but it’s an actual dilemma recently faced by...
Nylon 3D Printed Parts Made More Functional with Coatings & Colors
Parts 3D printed from polyamide (PA, Nylon) 12 using powder bed fusion (PBF) are a mainstay in the additive manufacturing (AM) industry. While post-finishing processes have improved the porosity of...
$25M to Back Sintavia’s Largest Expansion of Metal 3D Printing Capacity Since 2019
Sintavia, the digital manufacturing company specializing in mission-critical parts for strategic sectors, announced a $25 million investment to increase its production capacity, the largest expansion to its operations since 2019....
Velo3D Initiates Public Offering in a Bid to Strengthen Financial Foundations and Drive Future Growth
Velo3D (NYSE: VLD) has been among a number of publicly traded 3D printing firms that have attempted to weather the current macroeconomic climate. After posting a challenging financial report for 2023,...